RoHS – Do I need a High Tg Laminate?
Through the years, the printed wiring board industry has had to evolve in both materials and processes to meet the needs of the world’s electronic challenges. At first the laminate resin systems were inadequate to survive thru multiple thermal excursions of double-sided assembly and rework processes, then the need to meet the high speed signal integrity requirements were needed and now because of the environmentally friendly initiatives of RoHS have again asked the industry to step it up.
Currently most printed wiring boards can meet RoHS (Restriction of Hazardous Materials) directive requirements as long as the boards’ surface finish does not contain lead. Most if not all laminate manufacturers have already removed or reduced mercury, cadmium, hexavalent chromium, polybrominated biphenyls and polybrominated diphenyl ether levels to meet the directive. The challenge has been how to reliably attach components to the PWB without the use of lead, which have higher temperature and longer oven dwell times due to lead free metals being used. For this you need to look at the laminate materials Td rating (Time to Decomposition).
That’s right, even though material Tg has been the main focus of a laminates ability to survive temperature for years, it is not as important as the material’s Td.
Td is the measure of how long a material can handle the higher temperatures of the assembly process. Materials are more thermally resistant as evidenced by their higher Td rating and their ability to achieve a T260 or T288. A T260/288 (Time to Delamination) is the amount of time the material can withstand exposure to 260 / 288°C.
However, if you have a low cost double sided board that requires the use of lead free solder, it may not necessarily mean that you need the higher Tg/Td laminate. Talk to your assembler; you may be spending more than you need to on raw material costs, and being that laminate costs are the single highest material cost of the printed wiring board, it may be worth running some tests by subjecting boards to multiple Pb free reflow cycles to verify it’s resistance to delamination and blistering.
It is true that lead free solder does require higher reflow temperatures and longer dwell times but if the overall density of board is low, it will reflow faster because the entire structure heats up faster and does not require as long of a time in the assembly ovens to get up to the necessary reflow temperature to make a good solder joint, the lower Tg/Td material can reliably withstand the assembly process. Keep in mind that even standard 130dC Tg laminates made today are superior materials that meet RoHS requirements and work well for many different applications and in many cases can take a the thermal excursion of lead free assembly.
On the other hand if you have an expensive multilayer board that has a lot of copper planes, high density, it takes the structure much longer to heat up in order to reflow all the solder joints, in this case you need the extra assurance of high Td rated laminate systems.
If you have questions regarding materials or anything else PCB- Send us an email at info@pcb-solutions.com and we will be happy to guide you in the right direction. For more detailed information on Surface Finishes, visit our Surface Finish presentation in the Tech Zone at http://www.pcb-solutions.com/files/TECHZone-09-02-surface-finish.pdf
Please visit our home page at: www.pcb-solutions.com We are a supplier of Domestic and off-shore Rigid, Rigid-Flex and Flex Printed Circuit Boards (PCBs), Domestic Military PCBs, Domestic Tier I PCBA, Domestic Sheet Metal, Domestic Injection Molding and other Custom Fabricated Services.
http://www.pcb-solutions.com/pcb.html
http://www.pcb-solutions.com/flex.html
Bob Neisis
Quality Manager
PCB Solutions, LLC
Tags: Flex PCB, PCB, PCB Material, PCB Tg Td Rating, Printed Circuit Boards, PWB, Rigid Flex PCB